Question 15.2: An engineering component made of the heat-resisting Fe-Cr-Ni...

Mechanical Behavior of Materials

An engineering component made of the heat-resisting Fe-Cr-Ni-Co alloy S-590 is subjected in service to a static stress of 200 MPa at a temperature of 600°C. What creep–rupture life in days is expected?

The "Step-by-Step Explanation" refers to a detailed and sequential breakdown of the solution or reasoning behind the answer. This comprehensive explanation walks through each step of the answer, offering you clarity and understanding.
Our explanations are based on the best information we have, but they may not always be right or fit every situation.

The blue check mark means that this solution has been answered and checked by an expert. This guarantees that the final answer is accurate.
Learn more on how we answer questions.

This Question has been Answered.

Already have an account?

Related Answered Questions

Question: 15.8

A rectangular beam made of S-590 alloy has depth 2c = 50 mm and thickness b = 20 mm. It is loaded with a moment of M = 1.50 kN·m at a temperature of 725°C. At this temperature, and for stresses in the range 100 to 400 MPa, constants for Eq. 15.71 are m = 10.74 and B = 3.91 × 10^−29, where t is in ...

Verified Answer:

The stress at the edge of the beam is obtained dir...

Question: 15.7

A beam is simply supported over a length of L = 100 mm and is loaded at its center with a transverse load of P = 50 N. Its cross section has width b = 15 mm and depth 2c = 10 mm. The material has linear viscoelastic behavior with elastic and steady-state creep strains, similar to the model of ...

Verified Answer:

Due to the linear viscoelastic behavior, stresses ...

Question: 15.6

For a given material and temperature, the uniaxial creep behavior follows Eq. 15.39(b). A thin-walled tubular pressure vessel of radius r and wall thickness b has closed ends and is made of this material. Develop an equation for the relative change in radius, Δr/r , as a function of time t and a ...

Verified Answer:

we first generalize the uniaxial stress–strain cur...

Question: 15.5

Consider the situation of Ex. 15.2 and 15.3, where a component made of alloy S-590 is subjected to a stress of 200 MPa at a temperature of 600°C. (a) Repeat the rupture life calculation of Ex. 15.3, using the Eq. 15.20 fit for PLM. (b) If the desired service life is 1.5 years, what are the safety ...

Verified Answer:

(a) From Table 15.3, the S-590 alloy constants for...

Question: 15.4

The creep–rupture data for alloy S-590 plotted in Fig. 15.8 are given in Table E15.4(a), where, for each test, the temperature T, stress σ, and rupture time tr are listed. Employ these data as follows: (a) On the basis of Eq. 15.19, obtain a fitted equation relating the Sherby–Dorn parameter to ...

Verified Answer:

(a) First calculate x = log σ and

P_{SD}[/l...

Question: 15.3

Consider again Example 15.2, using the Larson–Miller parameter. ...

Verified Answer:

The logic is the same as before, except that now [...

Question: 15.1

Consider nickel with the same grain size and processing as the material of Fig. 15.16. This material is subjected to a tensile stress of 6 MPa at a temperature of 900°C. What is the approximate strain rate, and what creep mechanism is dominant? ...

Verified Answer:

To enter the map, we need τ and G from Eqs. 15.12 ...

Question: 15.9

Consider a rectangular beam of depth 2c, thickness b, and length L, that is subjected to a cyclic pure bending moment Ma about zero mean. The strains are sufficiently large that a nonlinear stress distribution occurs, and the material follows a cyclic stress–strain curve of the Ramberg–Osgood form, ...

Verified Answer:

The damping energy in the member is obtained by co...